Composite inorganic particles and methods of making and using the same

ABSTRACT

Composite inorganic particles and compositions containing silica particles are disclosed. Methods of making silica particles and methods of using composite inorganic particles are also disclosed.

FIELD OF THE INVENTION

This application is a divisional of U.S. patent application Ser. No.13/519748, which is a continuation of U.S. Provisional PatentApplication Ser. No. 61/290,748.

The present invention is directed to composite inorganic particles,compositions containing composite inorganic particles, methods of makingcomposite inorganic particles, and methods of using composite inorganicparticles.

BACKGROUND OF THE INVENTION

In various applications:, metal oxide particles containing metalphosphate are highly desired. For example, coatings having metalphosphate materials may he applied to a variety of substrates for avariety of purposes such as corrosion resistance against harsh chemicalenvironments at elevated temperatures, as fiber coatings to providetoughening of high temperature composites, as coatings for bio-activesurfaces for implants, and, in general, for surface modification of asubstrate to obtain desirable electrical, chemical, thermal andmechanical properties.

Efforts continue in the art to develop particles, such as metal oxideparticles containing metal phosphate, having optimum properties so thatthe particles may be utilized in a variety of applications.

There is a need in the art for metal oxide particles containing metalphosphate that are stable in a dispersion or suspension. Moreover, thereis a need in the art for metal oxide particles containing metalphosphate that are relatively small and/or uniform in size.

SUMMARY OF THE INVENTION

The present invention addresses some of the difficulties and problemsdiscussed above by the discovery of new composite inorganic particlescontaining metal phosphate. The composite inorganic particles have aparticle size and particle size distribution, which allows them toremain in suspension for long periods of time. Moreover, the compositeinorganic particles possess a composition and structure that provide fordesirable amounts of available, metal phosphate that is uniformlydistributed on the surface of the particles. The new composite inorganicparticles are typically porous or non-porous, a metal oxide particles,and may be used as anti-corrosion agents, fillers, hardening agents,surface modification agents, and the like. The new composite inorganicparticles are particularly suitable for use in anti-corrosion coatings,paints, bio-active surface coatings, protective coatings, filters fordental implants, fillers for ceramics, dopants for glasses, and thelike.

In one exemplary embodiment, a powder of composite inorganic particlesof the present invention comprises metal phosphate and metal oxidewherein the particles have a metal oxide core and a coating of metalphosphate on the metal oxide core.

In another exemplary embodiment, a powder of composite inorganicparticles of the present invention comprises metal oxide and metalphosphate particles having a particle size distribution such that themedian particle size is less than about 50 μm. The mean particle sizemay be about 40 μm or less, about 30 μm or less, or from about 20 μm orless. The median particle size may range about 0.001 μm to about 50 μm,from about 0.001 μm to about 40 μm, or about 0.001 μm to about 30 μm.

In an even further exemplary embodiment, a powder of composite inorganicparticles of the present invention comprises metal phosphate and metaloxide, wherein after being mixed with a liquid, forms a dispersion thatremains stable for at least six months. In an alternative, embodiment,the dispersion remains stable for at least about one year.

In one exemplary embodiment, a dispersion of composite inorganicparticles of the present invention comprises metal phosphate and metaloxide wherein the particles have a metal oxide core and a coating ofmetal phosphate on the metal oxide core.

In a further exemplary embodiment, a dispersion of composite inorganicparticles of the present invention comprises metal phosphate and metaloxide wherein the dispersion remains stable for at least six months. Inan alternative, embodiment, the dispersion remains stable for at leastabout one year.

The present invention is also directed to methods of making compositeinorganic particles. In another exemplary embodiment according to thepresent invention, the method of making composite inorganic particlescomprises providing a metal oxide particles, forming a coating of metalphosphate on the metal oxide particles.

In another exemplary embodiment according to the present invention, themethod of making composite inorganic particles comprises providing metaloxide particles, forming a coating of metal phosphate on the metal oxideparticles. The composite inorganic particles may have a particle sizedistribution such that the median particle size is less than about 50μm.

In one exemplary embodiment according to the present invention, themethod of making composite inorganic particles comprises providing metaloxide particles, forming a coating of metal phosphate on the metal oxideparticles. The dispersion may remain stable for at least six months, andeven up to more than a year.

The present invention is further directed to methods of using compositeinorganic particles. In one exemplary method of using compositeinorganic particles, the method comprises providing a powder ofcomposite inorganic particles comprising metal phosphate and metaloxide; mixing the powder with a liquid to form a dispersion; andapplying the dispersion to a substrate, wherein the particles have ametal oxide core and a coating of metal phosphate on the metal oxidecore.

In another exemplary method of using composite inorganic particles, themethod comprises providing a dispersion of liquid and compositeinorganic particles, which comprise metal phosphate and metal oxide: andapplying the dispersion to a substrate, wherein the particles have ametal oxide core and a coating of metal phosphate on the metal oxidecore.

These and other features and advantages of the present invention willbecome apparent after a review of the following detailed description ofthe disclosed embodiments and the appended claims.

DETAILED DESCRIPTION OF THE INVENTION

To promote an understanding of the principles of the present invention,descriptions of specific embodiments of the invention follow andspecific language is used to describe the specific embodiments. It willnevertheless be understood that no limitation of the scope of theinvention is intended by the use of specific language. Alterations,further modifications, and such further applications of the principlesof the present invention discussed are contemplated as would normallyoccur to one ordinarily skilled in the art to which the inventionpertains.

The present invention is directed to composite inorganic particles. Thepresent invention is further directed to methods of making compositeinorganic particles, as well as methods of using composite inorganicparticles. A description of exemplary composite inorganic particles,methods of making composite inorganic particles, and methods of usingcomposite inorganic particles are provided below.

It must be noted that as used herein and in the appended claims, thesingular forms “a”, “and”, and “the” include plural referents unless thecontext clearly dictates otherwise. Thus, for example, reference to “anoxide” includes a plurality of such oxides and reference to “oxide”includes reference to one or more oxides and equivalents thereof knownto those skilled in the art, and so forth.

“About” modifying, for example, the quantity of an ingredient in acomposition, concentrations, volumes, process temperatures, processtimes, recoveries or yields, flow rates, and like values, and rangesthereof, employed in describing the embodiments of the disclosure,refers to variation in the numerical quantity that can occur, forexample, through typical measuring and handling procedures; throughinadvertent error in these procedures: through differences in theingredients used to carry out the methods; and like proximateconsiderations. The term “about” also encompasses amounts that differdue to aging of a formulation with a particular initial concentration ormixture, and amounts that differ due to mixing or processing aformulation with a particular initial concentration or mixture. Whethermodified by the term “about” the claims appended hereto includeequivalents to these quantities.

As used herein, the term “inorganic” means compounds that typically donot contain carbon atoms, except for some carbon containing compounds,such as for example, carbon monoxide, carbon dioxide, carbonates,cyanides, cyanates, carbides, and thyocyanates, inorganic materialsinclude, but are not limited to, oxides, sulfides, hydroxides,carbonates, silicates, phosphates, etc, and mixtures thereof.

As used herein, “metal oxides”is defined as binary oxygen compoundswhere the metal is the cation and the oxide is the anion. The metals mayalso include metalloids. Metals include those elements on the left ofthe diagonal line drawn from boron to polonium on the periodic table.Metalloids or semi-metals include those elements that are on this line.Examples of metal oxides include silica, alumina, titania, zirconia,etc., and mixtures thereof.

As used herein the term “porous particles” means particles havingsignificant internal porosity as measured by nitrogen porisimetry, i.e.,a porosity of more than about 0.05 cc/g, and the term “non-porous” meansparticles having little or no internal porosity, i.e., an internalporosity of less than about 0.05 cc/g. Examples of porous particlesinclude, silica gel, precipitated silica, fumed silica, boehrnitealumina, etc., and examples of non-porous particles include colloidalsilica, alumina, titania, etc.

The composite inorganic particles of the present invention have aphysical structure and properties that enable the composite inorganicparticles to provide one or more advantages when compared to knowncomposite inorganic particles. The present invention addresses some ofthe difficulties and problems discussed above by the discovery of newcomposite inorganic particles containing metal phosphate and metaloxide. The composite inorganic particles have properties, which provideimproved stability when the composite inorganic particles are dispersedin a liquid. The composite inorganic particles have a particle size andparticle size distribution, which allows them to remain in suspensionfor long periods of time. Moreover, the composite inorganic particlespossess a composition and structure that provide for desirable amountsof available metal phosphate that is uniformly distributed on thesurface of the particles. The new composite inorganic particles aretypically porous or nonporous metal oxide and metal phosphate particles,and may be used as anti-corrosion agents, fillers, hardening agents,surface modification agents, and the like. The new composite inorganicparticles are particularly suitable for use in anti-corrosion coatings,paints, bio-active surface coatings, protective coatings, fillers fordental implants, fillers for ceramics, dopants for glasses, and thelike.

In one exemplary embodiment, a powder of composite inorganic particlesof the present invention comprises metal phosphate and metal oxidewherein the particles have a metal oxide core and a coating of metalphosphate on the metal oxide core.

In another exemplary embodiment, a powder of composite inorganicparticles of the present invention comprises metal oxide and metalphosphate particles having a particle size distribution such that themedian particle size is less than about 50 μm. In a further exemplaryembodiment, the mean particle size may be about 40 μm or less, about 30μm or less, or from about 20 μm or less. In an even further embodiment,the median particle size may range about 0.001 μm to about 50 μm, fromabout 0.001 μm to about 40 μm, or about 0.001 μm to about 30 μm.

In an even further exemplary embodiment, a powder of composite inorganicparticles of the present invention comprises metal phosphate and metaloxide, wherein after being mixed with a liquid, forms a dispersion thatremains stable for at least six months. In an alternative, embodiment,the dispersion remains stable for at least about one year.

In one exemplary embodiment, a dispersion of composite inorganicparticles of the present invention comprises metal phosphate and metaloxide wherein the particles have a metal oxide core and a coating ofmetal phosphate on the metal oxide core.

In a further exemplary embodiment, a dispersion of composite inorganicparticles of the present invention comprises metal phosphate and metaloxide wherein the dispersion remains stable for at least six months. Inan alternative, embodiment, the dispersion remains stable for at leastabout one year,

In one exemplary embodiment, a composite particle of the presentinvention comprises composite inorganic particles having a particle sizedistribution such that the mean particle size is about 50 μm or less.The particle size distribution may be such that the mean particle sizeis about 49 μm or less, about 48 μm or less, about 47 μm or less, 46 μmor less, 45 μm or less, 44 μm or less, 43 μm or less, 42 μm or less, 41μm or less, 40 μm or less, 39 μm or less, 38 μm or less, 37 μm or less,36 μm or less, 35 μm or less, 34 μm or less, 33 μm or less, 32 μm orless, 31 μm or less, 30 μm or less. In another exemplary embodiment, themedian particle size of the composite particle may range about 0.001 μmto about 50 μm, from about 0,001 μm to at 40 μm, or about 0.001 μm toabout 30 μm.

In another exemplary embodiment where porous materials are utilized, thecomposite inorganic particles of the present invention may have a porevolume as measured by nitrogen porosimetry of at least about 0.40 cc/g.In one exemplary embodiment of the present invention, the compositeinorganic particles have a pore volume as measured by nitrogenporosimetry of from about 0.40 cc/g to about 1.4 cc/g. In anotherexemplary embodiment of the present invention, the composite inorganicparticles have a pore volume as measured by nitrogen porosimetry of fromabout 0.75 cc/g to about 1.1 cc/g. An added benefit of using porousmetal oxide core particles provides desirable amounts of metal phosphatethat may be readily solubilized and allows for improved interaction withcomponents in formulations made therefrom.

In one exemplary embodiment, composite inorganic particles of thepresent invention may have a surface area as measured by the BETnitrogen adsorption method (i.e., the Brunauer Emmet Teller method) ofat least about 150 m²/g. In another exemplary embodiment of the presentinvention, the composite inorganic particles have a BET surface area offrom about 400 m²/g to about 700 m²/g. in a further exemplary embodimentof the present invention, the composite inorganic particles have a BETsurface area of from about 450 m²/g to about 500 m²/g.

In another exemplary, embodiment, the metal oxide core comprises anyporous or nonporous particles formed via any known process including,but not limited to, a solution polymerization process such as forforming colloidal particles, a continuous flame hydrolysis techniquesuch as for forming fused particles, a gel technique such as for forminggelled particles, and a precipitation technique such as for formingprecipitated particles. The particles may be composed of inorganicmaterials. In one exemplary embodiment the core particles are composedof inorganic materials such as metal oxides, sulfides, hydroxides,carbonates, silicates, phosphates, etc, but are preferably metal oxides.The particles may be a variety of different symmetrical, asymmetrical orirregular shapes, including chain, rod or lath shape. The particles mayhave different structures including amorphous or crystalline, etc. Theparticles may include mixtures of particles comprising differentcompositions, sizes, shapes or physical structures, or that may be thesame except for different surface treatments,

In one embodiment, the metal oxide core particulates comprises porousmaterials, such as precipitated metal oxide (e.g., silica, alumina,titanic, etc.), metal oxide gel, or fumed metal oxide. As it is wellknown in the art, the formation of precipitated silica occurs in areaction between waterglass and an acid via first forming a seed ofprimary particles which can be grown to larger particles, followed by anaggregation and then by an agglomeration of these aggregates. Dependingon the reaction conditions, the agglomerates can be grown even moretogether by a so called reinforcement. At a certain agglomerate size andconcentration, the hydrous silica begins to settle from the reactionslurry as a precipitate. To isolate the hydrous silica from the slurryand to remove the reaction electrolyte from the crude silica, theprecipitate is filtered from the slurry and washed. The resulting filtercake then is dried using drying equipment as known in the art. Dependingon the method and extend of drying, a stiffening of the silica structurewill occur during the drying step in which irreversible Si—O—Si-linksare formed from initial silanol groups, Processes for makingprecipitated metal oxides include those set forth in U.S. Pat. Nos.7,037,47581; 5,030,286 and 4,157,920, the entire subject matter of whichis incorporated herein by reference. In a further embodiment of thepresent invention, the metal oxide particles stem from the primaryparticles, grown particles, aggregated particles, agglomerated particlesor the filter cake of a general metal oxide precipitation process asdescribed above.

Methods of preparing metal oxide gels are well known in the art andinclude those set forth in U.S. Pat. No. 6,380,265, the entire subjectmatter of which is incorporated herein by reference. For example, asilica gel is prepared by mixing an aqueous solution of an alkali metalsilicate (e.g., sodium silicate) with a strong acid such as nitric orsulfuric acid, the mixing being done under suitable conditions ofagitation to form a clear silica sol which sets into a hydrogel, i.e.,macrogel, in less than about one-half hour. The resulting gel is thenwashed. The concentration of metal oxide, i.e., SiO₂, formed in thehydrogel is usually in the range of about 10 and about 50 weightpercent, With the pH of that gel being from about 1 to about 9,preferably 1 to about 4. A wide range of mixing temperatures can beemployed, this range being typically from about 20 to about 50′C. Thenewly formed hydrogels are washed simply by immersion in a continuouslymoving stream of water which leaches out the undesirable salts, leavingabout 99.5 weight percent or more pure metal oxide behind. The pH,temperature, and duration of the wash water will influence the physicalproperties of the silica. such as surface area (SA) and pore volume(PV). Silica gel washed at 65-90° C. at pH's of 8-9 for 15-36 hours willusually have SA's of 250-400 and form aerogels with PV's of 1.4 to 1.7cc/gm. Silica gel washed at pH's of 3.5 at 50-65° C. for 15-25 hourswill have SA's of 700 850 and form aerogels with PV's of 0.6-13 Thesemeasurements are generated by N₂ porosity analysis. Methods forpreparing metal oxide gels such as alumina and mixed metal oxide gelssuch as silica/alumina cogels are also well known in the art. Methodsfor preparing such gels are disclosed in U.S. Pat. No. 4,226,743, thecontents of which are incorporated by reference. In general, aluminagels are prepared by mixing alkali metal aluminates and aluminumsulfate. Cogels are prepared by cogelling two metal oxides so that thegels are composited together. For example, silica alumina cogels can beprepared by gelling an alkali metal silicate with an acid or acid salt,and then adding alkali metal aluminate, aging the mixture andsubsequently adding aluminum sulfate. The gel is then washed usingconventional techniques.

In another exemplary embodiment, the metal oxide particles comprisenonporous metal oxides, such as colloidal metal oxide particles.Colloidal metal oxides include those particles originating fromdispersions or sols in which the particles do not settle from dispersionover relatively long periods of time. Such particles are typically belowone micron in size. Colloidal metal oxides having an average particlesize in the range of about 1 to about 300 nanometers and processes formaking the same are well known in the art. See U.S. Pat. Nos. 2,244,325;2,574,902; 2,577,484; 2,577,485; 2.631.134; 2,750,345; 2,892,797;3,012,972; and 3,440,174, the contents of which are incorporated hereinby reference. In an exemplary embodiment, the colloidal metal oxideparticles may be colloidal silicas having average particle sizes in therange of 5 to 100 nanometers, Colloidal silicas can have a surface area(as measured by BET) in the range of 9 to about 2700 m²/g.

In one exemplary embodiment, the metal oxide core particles possess amean particle size of about 40 μm or less, about 30 μm or less, or about20 μm or less, In another exemplary embodiment, the metal oxide coreparticles possess a median particle size range from about 0.001 μm toabout 50 μm, from about 0.001 μm to about 40 μm, or from about 0.001 μmto about 30 μm. In a further exemplary embodiment, the metal oxide coreparticles possess a mean particle size of about 10 microns or less, orabout 9, 8, 7, 6, 5, 4, 3, 2 or even 1 microns or less.

In an exemplary embodiment, the composite inorganic particles includethe metal oxide core with a coating comprising metal phosphate formedthereon, The coating may be continuous or discontinuous. In oneembodiment, the metal phosphate may be calcium phosphate. The amount ofmetal phosphate deposited on the metal oxide core varies depending onthe reaction conditions. For example, in one embodiment, the compositeinorganic particles comprise weight of metal to weight of metal oxideratio (wtM/wtMO_(x)) of about 0.001 to about 0.5 in the compositeinorganic particles, or from about 0.001 to about 0.4 or from about0.001 to about 0.3, or even from about 0.001 to about 0.2.

The present invention is also directed to methods of making compositeinorganic particles. in one exemplary embodiment according to thepresent invention, the method of making composite inorganic particlescomprises providing metal oxide particles, forming a coating of metalphosphate on the metal oxide particles.

In another exemplary embodiment according to the present invention, themethod of making composite inorganic particles comprises providing metaloxide particles, forming a coating of metal phosphate on the metal oxideparticles. The composite inorganic particles may have a particle sizedistribution such that the median particle size is less than about 50μm. in one exemplary embodiment, the metal oxide core particles possessa mean particle size of about 40 μm or less, about 30 μm or less, orabout 20 μm or less. In another exemplary embodiment, the metal oxidecore particles possess a median particle size range from about 0.001 μmto about 50 μm, from about 0.001 μm to about 40 μm, or from about 0.001μm to about 30 μm.

In one exemplary embodiment according to the present invention, themethod of making composite inorganic particles comprises providing metaloxide particles, forming a coating of metal phosphate on the metal oxideparticles. The dispersion may remain stable for at least six months, andeven up to more than a year.

In one embodiment, the metal oxide particles are formed prior toformation of the composite inorganic particles. Raw materials used toform the metal oxide particles and composite inorganic particles of thepresent invention, as well as method steps for forming the metal oxideparticles and composite inorganic particles of the present invention arediscussed below.

The methods of making metal oxide particles of the present invention maybe formed from a number of metal oxide-containing raw materials. Forexample, suitable raw materials for making silica include, but are notlimited to, metal silicates, such as alkali metal silicates. Dependingon what metal oxide particle is selected for the core material (e.g.,colloidal, fumed, precipitated, gel, etc.), the reactants and processconditions will vary as set forth herein.

For example, if silica gel is selected as the metal oxide coreparticles, they are prepared by the above-mentioned process for makinggels. After washing, the gel is dried. Drying rate has an effect on thesurface area and pore volume of the final metal oxide particles. In oneexemplary embodiment, the drying step comprises spreading a decantedvolume or filter cake of silica product into a tray so as to form asilica cake thickness of about 1.25 cm: placing the tray containing thesilica cake in a gravity convection oven for about 20 hours at an oventemperature of about 140° C; removing the tray and silica from the oven;and collecting the silica. The dried silica material is then milledand/or classified to prepare a powder having a mean particle size ofabout 50 μm or less. In one exemplary embodiment, the metal oxide coreparticles possess a mean particle size of about 40 μm or less, about 30μm or less, or about 20 μm or less. In another exemplary embodiment, themetal oxide core particles possess a median particle size range fromabout 0.001 μm to about 50 μm, from about 0.001 μm to about 40 μm, orfrom about 0.001 μm to about 30 μm. The particles are then ready forsubsequent preparation of the composite inorganic particles.

In another exemplary embodiment according to the present invention, themethod of making composite inorganic particles comprises forming adispersion of metal oxide core particles and adding solutions of metalsalts and phosphate salts thereto at a basic pH (e.g., 7-14) whilestirring the mixture. The mole ratio of metal salt to phosphate salt maybe any range, but in the range of 1.0 to 2.0. The metal and phosphatereagents may be added over a period of time, e.g., up to several hours,but is typically less than one hour The basic pH is maintained duringthe reaction with the appropriate bases, including but not limited to,potassium hydroxide, sodium hydroxide, ammonium hydroxide, etc., ormixtures thereof. The resulting slurry is washed andfiltered/ultrafiltered in order to remove any salts formed during thereaction. In exemplary embodiments where the composite inorganicparticles are nano-particles, the resulting slurry is stable for longperiods of time, even for more than one year. The metal content for themetal component in the resulting composite inorganic particles rangesfrom about 0.01 to about 0.50 based on the weight of metal oxide in thecomposite inorganic particles. The solids content in the resultingcomposite inorganic particle dispersions range from about 1 to about 40wt % based on the total weight of the dispersion. In an alternativeexemplary embodiment, the dispersions comprising composite inorganicparticulates are drained to form a filter cake and then dried, or aresimply spray dried.

The present invention is further directed to methods of using compositeinorganic particles. The composite inorganic particles may be used in avariety of applications, including as anticorrosion agents inanticorrosion coating applications, as pigments for other coatingapplications, as filler in biocompatible or ceramic applications, as anactive component in dental cements, as a hardener in protectivecoatings, as a surface modifier in coatings for surface modification ofa substrate to obtain desirable electrical, chemical, thermal andmechanical properties, and the like. In one exemplary method of usingmetal oxide particles, the method comprises providing a powder ofcomposite inorganic particles comprising metal phosphate and metaloxide; mixing the powder with a liquid to form a dispersion: andapplying the dispersion to a substrate, wherein the particles have ametal oxide core and a coating of metal phosphate on the metal oxidecore. In another exemplary method of using composite inorganicparticles, the method comprises providing a dispersion of liquid andcomposite inorganic particles, which comprise metal phosphate and metaloxide: and applying the dispersion to a substrate, wherein the particleshave a meta; oxide core and a coating of metal phosphate on the metaloxide core. The composite inorganic particles may have a particle sizedistribution such that the median particle size is less than about 50μm. The dispersion may include various other components and/or beutilized in other formulations depending upon the desired application.For example, if the composite inorganic particles are intended for usein an anticorrosion coating formulation, the composite inorganicparticles are added to the formulation as powder, dispersions or pastes.If the composite metal particles are utilized in dental cements, theymay be added as powder, dispersions or pastes.

The advantages of the composite inorganic particles of the presentinvention is provided by a particle size and particle size distribution,which allows them to remain in suspension for long periods of time.Moreover, the composite inorganic particles possess a composition andstructure that provide for desirable amounts of available metalphosphate that is uniformly distributed on the surface of the particles.

EXAMPLES

The present invention is further illustrated by the following examples,which are not to be construed in any way as imposing limitations uponthe scope thereof. On the contrary, it is to be clearly understood thatresort may be had to various other embodiments, modifications, andequivalents thereof which, after reading the description herein, maysuggest themselves to those skilled in the art without departing fromthe spirit of the present invention and/or the scope of the appendedclaims. The following examples reference silica, but any metal oxide maybe utilized in the present invention. In addition, even though calciumphosphate is referenced in the Examples, any metal phosphate may beutilized in the present invention.

Example 1

The colloidal silica is made using the process set forth in U.S. Pat.No. 2,631,134. In this example, the reaction is carried out by thesimultaneous addition of silicate and resin to a reaction vessel whilecontinuously withdrawing the silica sol thus formed. The reaction iscarried out in a four liter stainless steel beaker with an overflowpipe, which maintains the contents of the beaker at two liters; at theoutset the beaker is filled with water. A solution of sodium silicate(3.25 SiO₂:Na₂O, 10 per cent SiO₂) is fed into the beaker at a rate of25 ml./min. Simultaneously wet, drained “Amberlite® IRC-50” (hydrogenform) is fed into the beaker at such a rate as to maintain the pH at9±0.3. The temperature is maintained at about 60° C. The system isvigorously stirred during silicate addition. The overflow is droppedonto a filter and filtered immediately, the first two liters of filtratebeing discarded. The addition of resin and silicate is continued forseveral hours. The product is a silica sol having a particle size of 12nm, pH of about 9, a SiO₂:Na₂O ratio of about 100:1, and containingabout ten percent SiO₂. The sol is then concentrated to 40 percentsilica by evaporation at 100° C. 600 g of the colloidal silica slurry(40% SiO₂) is placed in a beaker. To this, three separate reagents areadded at the same time with good mixing using a conventional beakermixer. Ail additions are performed at room temperature. The fist reagent(2000 g) added to the mixture is a 3 wt % solution of Ca(NO₃)2.4 H₂O(based on the weight of the solution). The second reagent (1200 g) addedto the mixture is a 3 wt % solution of Na₂HPO₄. The third reagent addedto the mixture is a 2 wt % solution of NaOH. The calcium and phosphatereagents are added at such a rate as to add the full amounts in 40minutes. The pH is maintained at 9.5 by the appropriate addition ofNaOH, in this example, 355 g of the above-mentioned 2 wt % solution ofNaOH are used. Once ail of the reagents are added and the reaction iscomplete, the slurry is ultrafiltered in order to remove salts generatedduring the reaction. The final composite calcium phosphate silicaparticle dispersion is stable (i.e., the particles do not precipitate)and the particles possess a Ca/P mole ratio of 1.67 and a wtCa/wtSiO2 of0.04. The pH of the dispersion is 9.4 and the solids content is 21.3 wt% based on the total weight of the dispersion (obtained by drying at205° C. to constant weight). The dispersion remains stable for at leastsix months.

Example 2

The process of Example 1 is repeated but using half of the amounts ofcalcium nitrate and sodium phosphate. These reagents are added over aperiod of 19 minutes. The final composite calcium phosphate silicaparticle dispersion is stable and the particles possess a Ca/P moleratio of 1:68 and a wtCa/wtSiO₂ of 0.02. The pH of the dispersion is 9.3and the solids content is 19.2 wt % based on the total weight of thedispersion: The dispersion remains stable for at least six months.

Example 3

The process of Example 1 is repeated but using 800 g of 7 nm colloidalsilica slurry (30% SiO2) prepared by the process recited in Example 1.The smaller particles are formed by using less reaction time and thelower solids is provided using less evaporation time. The other amountsof reactants utilized are the same as those set forth in Example 1. Thefinal composite calcium phosphate silica particle dispersion is stableand the particles possess a Ca/P mole ratio of 1.71 and a wtCa/wtSiO₂ of0.04. The pH of the dispersion is 9.5 and the solids content is 21.6 wt% based on the total weight of the dispersion. The dispersion remainsstable for at least six months.

Example 4

The process of Example 3 is repeated but using half of the amounts ofcalcium nitrate and sodium phosphate. The other amounts of reactantsutilized are the same as those set forth in Example 1. The finalcomposite calcium phosphate silica particle dispersion is stable and theparticles possess a Ca/P mole ratio of 1.99 and a wtCa/wtSiO₂ of 0.02.The pH of the dispersion is 9.5 and the solids content is 21.6 wt %based on the total weight of the dispersion. The dispersion remainsstable for at least six months.

Example 5

Silica gel is made according to the process recited herein and in U.S.Pat. No. 6,380,265, For example, silica gel is prepared by mixing anaqueous solution of an alkali metal silicate (e.g., sodium silicate)with a sulfuric add, the mixing being done under suitable conditions ofagitation to form a dear silica sol which sets into a hydrogel, i.e.,macrogel, in less than about one-half hour. The resulting gel is thenwashed. The concentration of metal oxide, i.e., SiO₂, formed in thehydrogel is usually in the range of about 19 weight percent, with the pHof that gel being from about 1.5. A wide range of mixing temperaturescan be employed, this temperature being about 27° C. The newly formedhydrogels are washed simply by immersion in a continuously moving streamof water which leaches out the undesirable salts, leaving about 99.5weight percent or more pure metal oxide behind. Silica gel is washed atabout 80° C. at a pH of about 8 for about 25 hours. The silica gel isdrained, dried and then milled to form a powder having a surface area of270 m²/g, a pore volume of 1.2 cc/g and a median particle size of 6microns. 528 g of the silica powder is dispersed in 792 g of deionizedwater and the pH is adjusted to 9.5 with 2 wt % sodium hydroxide. Alladditions are performed at room temperature. Then 2200 g of 3 wt % ofCa(NO₃)2.4 H₂O and 880 g of 3 wt % of Na₂HPO₄ is added simultaneouslyover a period of 39 minutes. The pH of the slurry is maintained at 9.5by the appropriate addition of 2 wt % NaOH. 517 g of 2 wt % NaOH areused for this purpose. Then the slurry is filtered and washed threetimes with 550 mL of deionized water. The filter cake is redispersed indeionized water and then spray dried. The final powder has a wtCa/wtSiO2of 0.06.

These Examples demonstrate that the composite inorganic (e.g., metalphosphate metal oxide) particles of the present invention provide stableparticle dispersions having sufficient amount of metal phosphatetherein. These dispersions produce desirable formulations havingadvantageous levels of metal phosphate, which may be utilized in avariety of applications, including but not limited to, medical, dental,anticorrosion, and paint applications.

While the invention has been described with a limited number ofembodiments, these specific embodiments are not intended to limit thescope of the invention as otherwise described and claimed herein. it maybe evident to those of ordinary skill in the art upon review of theexemplary embodiments herein that further modifications, equivalents,and variations are possible. All parts and percentages in the examples,as well as in the remainder of the specification, are by weight unlessotherwise specified. Further, any range of numbers recited in thespecification or claims, such as that representing a particular set ofproperties, units of measure, conditions, physical states orpercentages, is intended to literally incorporate expressly herein byreference or otherwise, any number falling within such range, includingany subset of numbers within any range so recited. For example, whenevera numerical range with a lower limit, R_(L), and an upper limit R_(U),is disclosed, any number R falling within the range is specificallydisclosed. In particular, the following numbers R within the range arespecifically disclosed: R=R_(L)+_(k)(R_(U)-R_(L)), where k is a variableranting from 1% to 100% with a 1% increment, e.g., k is 1%, 2%, 3%, 4%,5%. . 50%, 51%, 52%, 95%, 96%, 97%, 98%, 99%, or 100%. Moreover, anynumerical range represented by any two values of R, as calculated aboveis also specifically disclosed. Any modifications of the invention, inaddition to those shown and described herein, will become apparent tothose shifted in the art from the foregoing description and accompanyingdrawings. Such modifications are intended to fail within the scope ofthe appended claims.

What is claimed is:
 1. A powder of composite inorganic pattiescomprising: particles comprising metal phosphate and metal oxide;wherein the particles comprise a metal oxide core with metal phosphateformed thereon.
 2. The powder of claim 1, wherein the metal phosphatecomprises calcium phosphate, magnesium phosphate and mixtures thereof.3. The powder of claim 1, wherein the metal oxide comprises silica,alumina, titanic, zirconia, and mixtures thereof.
 4. The powder of claim1 wherein the metal oxide comprises nano-particles.
 5. The powder ofclaim 1, wherein the composite inorganic particles comprise a weight ofmetal to weight of metal oxide ratio of about 0.001 to about 0.5. 6.Composite inorganic particles comprising, a metal oxide core with metalphosphate formed thereon; wherein said particles comprise a particlesize distribution such that the median particle size is less than about50 μm.
 7. The inorganic particles of claim 6, wherein the metalphosphate comprises calcium phosphate, magnesium phosphate, and mixturesthereof.
 8. The inorganic particles of claim 6, wherein the metal oxidecomprises silica, alumina, titanic, zirconia and mixtures thereof. 9.The inorganic particles of claim 6, wherein the particle sizedistribution such that the median particle size ranges from about 0.001μm to about 40 μm.
 10. The inorganic particles of claim 6, wherein theparticle size distribution such that the median particle size rangesfrom about 0.001 μm to about 30 μm.
 11. The inorganic particles of claim6, wherein the metal oxide comprises nanoparticles.
 12. The inorganicparticles of claim 6, wherein the composite inorganic particles comprisea weight of metal to weight of metal oxide ratio of about 0.001 to about0.5.
 13. A method of making composite inorganic particles, said methodcomprising the steps of: (a) providing a dispersion of metal oxideparticles: (b) providing a solution of metal phosphate precursors; (c)mixing the solution of metal phosphate precursors with the metal oxideparticles; and (d) depositing metal phosphate from the metal phosphateprecursors on the metal oxide to form the composite inorganic oxideparticles.
 14. The method of making composite inorganic particles ofclaim 13, wherein the metal phosphate comprises calcium phosphate,magnesium phosphate, and mixtures thereof.
 15. The method of makingcomposite inorganic particles of claim 13, wherein the metal oxidecomprises silica, alumina, titanic, zirconia, and mixtures thereof. 16.The method of making composite inorganic particles of claim 13, whereinthe dispersion remains stable for at least six months.
 17. The method ofmaking composite inorganic particles of claim 13, wherein the dispersionremains stable for at least twelve months.
 18. The method of makingcomposite inorganic particles of claim 13, wherein the metal oxidecomprises nano-particles.
 19. The method of making composite inorganicparticles of claim 13, wherein the composite inorganic particlescomprise a weight of metal to weight of metal oxide ratio of about 0.001to about 0.5.
 20. Composite inorganic particles formed by the method ofclaim 13.